Sv-X12NMBF (X12NMBF)
Einstufung
| Land | Abschnitt | Kategorie |
|---|---|---|
| GUS, Russland, Ukraine | Aluminium, Aluminiumlegierungen | Geschmiedete Aluminiumlegierungen |
Chemische Zusammensetzung
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | V, % | P, % | C, % | S, % | Nb, % | Mo, % |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 83.96–87.5 | < 0.6 | < 0.6 | 10.5–12 | 1.4–1.8 | 0.15–0.25 | < 0.03 | 0.05–0.09 | < 0.02 | 0.05–0.15 | 0.35–0.5 |
Informationen zum Lieferanten
Properties
| Property |
|---|
| Performance data Application temperature: <600 ° C |
| Reference data Temperature: 20 ° C; Yield Strength:> 480 MPa |
| Reference data Temperature: 20 ° C; Temporary resistance:> 576 MPa |
| Reference data Temperature: 20 ° C Elongation:> 15% |
| Reference data Temperature: 20 ° С; Relative narrowing:> 50% |
| Temperature: 500 ° C; Yield Strength:> 352 MPa |
| Temperature: 500 ° C; Temporary resistance:> 412 MPa |
| Temperature: 500 ° C; Elongation:> 11% |
| temperature: 500 ° C; Relative contraction:> 50% |
| Temperature: 550 ° C; Yield Strength:> 325 MPa |
| Temperature: 550 ° C; Temporary resistance:> 366 MPa |
| Temperature: 550 ° C Elongation:> 13% |
| Temperature: 550 ° C; Relative narrowing:> 55% |
| Temperature: 500 - 600 ° C; Yield Strength:> 283 MPa |
| Temperature: 500 - 600 ° C; Temporary resistance:> 304 MPa |
| Temperature: 500 - 600 ° C; Elongation:> 14% |
| Temperature: 500 - 600 ° C; Relative narrowing:> 60% |
| Calculated Properties Density: 7.79 g / cm3 |
Beschreibung der chemischen Elemente
| Element | Maßeinheiten | Beschreibung |
|---|---|---|
| Fe | % | Eisen |
| Si | % | Silizium |
| Mn | % | Mangan |
| Cr | % | Chrom |
| Ni | % | Nickel |
| V | % | Vanadium |
| P | % | Phosphor |
| C | % | Kohlenstoff |
| S | % | Schwefel |
| Nb | % | Niob |
| Mo | % | Molybdän |